The research effort in mesoporous p-type semiconductors is increasing due to their potential application in photoelectrochemical energy conversion devices. In this paper an electron-hole pair is created by band-gap excitation of NiO nanoparticles and the dynamics of the electron and the hole is followed until their recombination. By spectroscopic characterization it was found that surface Ni³⁺ states work as traps for both electrons and holes. The trapped electron was assigned to a N²⁺ state and the trapped hole to a Ni⁴⁺ state. The recombination kinetics of these traps was studied and related with the concept of hole relaxation suggested before.The timescale of the hole relaxation was foundto be in the order of tens of ns. Finally the spectrosc opic evidence of this relaxation is presented in a sensitized film.

The anchoring group of a sensitizer may strongly affect the overall properties and stability of the resulting dye-sensitized solar cells (DSSCs) and dye-sensitized photoelectrosynthetic solar cells (DSPECs). The properties of seven perylene monoimide (PMI) dyes have been comprehensively studied for their immobilization on nanocrystalline NiO film. The PMI dyes differ only by the nature of the anchoring group, which are: carboxylic acid (PMI-CO2H), phosphonic acid (PMI-PO3H2), acetyl acetone (PMI-acac), pyridine (PMI-Py), aniline (PMI-NH2), hydroxyquinoline (PMI-HQ), and dipicolinic acid (PMI-DPA). The dyes are investigated by cyclic voltammetry and spectroelectrochemistry and modeled by TD-DFT quantum chemical calculations. The mode of binding of these anchoring groups is investigated by infrared spectroscopy and the stability of the binding to NiO surface is studied by desorption experiments in acidic and basic media. The phosphonic acid group is found to offer the strongest binding to the NiO surface in terms of stability and dye loading. Finally, a photophysical study by ultrafast transient absorption spectroscopy shows that all dyes inject a hole in NiO with rate constants on a subpicosecond timescale and display similar charge recombination kinetics. The photovoltaic properties of the dyes show that PMI-HQ and PMI-acac give the highest photovoltaic performances, owing to a lower degree of aggregation on the surface.

A series of bis-tridentate ruthenium complexes was designed to feature opposite localizations of their lowest metal-to-ligand charge transfer (MLCT) excited states, relative to a carboxylic acid that served as a binding group to mesoporous NiO. The purpose was to study the effect of MLCT direction on the rates of hole injection into NiO and subsequent charge recombination. Surprisingly, femtosecond-transient absorption spectroscopy showed that the two heteroleptic, cyclometalated complexes of this series did not inject holes into NiO, but their excited states were nevertheless quenched in a rapid process (on the time scale of hundreds of picoseconds). An identical result was obtained for the dyes on nonreactive ZrO₂ and we therefore attribute the short MLCT lifetime to self-quenching, due the high surface concentrations of the dyes. We further show that self-quenching on this time scale can potentially compete with hole injection also for functional NiO sensitizers. A ruthenium polypyridine complex, which has previously been used for NiO-based solar cells, was shown to inject holes only very slowly (τ ≈ 5 ns), in contrast to the common notion that hole injection in dye-NiO systems is ultrafast (predominantly subpicosecond time scale). The hole injection yield was estimated to only ca. 20%, which matches the reported APCE value of the corresponding device [Freys, J. C.; Gardner, J. M.; D’Amario, L.; Brown, A. M.; Hammarström, L. Dalton Trans. 2012, 41, 13105]. Therefore, we suggest that slow injection and self-quenching might be a reason for the low photovoltaic performance of some p-type dye-sensitized solar cells.

In this study, a core-shell NiO-dye-TiO2 mesoporous film was fabricated for the first time, utilizing atomic layer deposition technique and a newly designed triphenylamine dye. The structure of the film was confirmed by SEM, TEM, and EDX. Excitation of the dye led to efficient and fast charge separation, by hole injection into NiO, followed by an unprecedentedly fast dye regeneration (t1/2 [less-than-or-equal] 500 fs) by electron transfer to TiO2. The resulting charge separated state showed a pronounced transient absorption spectrum caused by the Stark effect, and no significant decay was found within 1.9 ns. This indicates that charge recombination between NiO and TiO2 is much slower than that between the NiO and the reduced dye in the absence of the TiO2 layer (t1/2 [approximate] 100 ps).

A ruthenium complex, porphyrin sensitizer, fullerene acceptor molecular pentad has been synthesized and a long-lived hole–electron pair was achieved in aqueous solution by photoinduced multistep electron transfer: Upon irradiation by visible light, the excited-state of a zinc porphyrin (¹ZnP*) was quenched by fullerene (C₆₀) to afford a radical ion pair, ^1,3(ZnP^.+-C₆₀^.−). This was followed by the subsequent electron transfer from a water oxidation catalyst unit (Ru^II) to ZnP^.+ to give the long-lived charge-separated state, Ru^III-ZnP-C₆₀^.−, with a lifetime of 14 μs. The ZnP worked as a visible-light-harvesting antenna, while the C₆₀ acted as an excellent electron acceptor. As a consequence, visible-light-driven water oxidation by this integrated photosynthetic model compound was achieved in the presence of sacrificial oxidant and redox mediator.