Alloy 247LC is sensitive to cracking during laser beam powder bed fusion (PBF-LB) manufacturing. Post processing is thus required to close cracks and achieve desired properties. In this study, samples of Alloy 247LC were manufactured by PBF-LB and subsequently post processed by hot isostatic pressing (HIP), HIP + solution and ageing heat treatments. The microstructure was characterized. Results showed cracks in the as-built condition. Cracks were not detected after HIP. Bright microconstituents were observed in the region between the cells, mainly, because of the partitioning of Hf and Ta into the intercellular region, where they presumably form carbides. What is assumed to be oxides were prominent in the microstructure. Thermodynamic calculations showed rapid formation of ?’ precipitates in the alloy, due to the high total concentration of Al and Ta and this was linked to the high hardness values in the as-built condition. © 2019 MS&T19®

The manufacturing of parts from nickel-based superalloy Alloy 247LC by laser powder bed fusion (L-PBF) is challenging, primarily owing to the alloy’s susceptibility to cracks. Apart from the cracks, voids created during the L-PBF process should also be minimized to produce dense parts. In this study, samples of Alloy 247LC were manufactured by L-PBF, several of which could be produced with voids and crack density close to zero. A statistical design of experiments was used to evaluate the influence of the process parameters, namely laser power, scanning speed, and hatch distance (inherent to the volumetric energy density) on void formation, crack density, and microhardness of the samples. The window of process parameters, in which minimum voids and/or cracks were present, was predicted. It was shown that the void content increased steeply at a volumetric energy density threshold below 81 J/mm3. The crack density, on the other hand, increased steeply at a volumetric energy density threshold above 163 J/mm3. The microhardness displayed a relatively low value in three samples which displayed the lowest volumetric energy density and highest void content. It was also observed that two samples, which displayed the highest volumetric energy density and crack density, demonstrated a relatively high microhardness; which could be a vital evidence in future investigations to determine the fundamental mechanism of cracking. The laser power was concluded to be the strongest and statistically most significant process parameter that influenced void formation and microhardness. The interaction of laser power and hatch distance was the strongest and most significant factor that influenced the crack density. © 2020 by the authors.

This paper reviews state of the art laser powder bed fusion (L-PBF) manufacturing of γ′ nickel-based superalloys. L-PBF resembles welding; therefore, weld-cracking mechanisms, such as solidification, liquation, strain age, and ductility-dip cracking, may occur during L-PBF manufacturing. Spherical pores and lack-of-fusion voids are other defects that may occur in γ′-strengthened nickel-based superalloys manufactured with L-PBF. There is a correlation between defect formation and the process parameters used in the L-PBF process. Prerequisites for solidification cracking include nonequilibrium solidification due to segregating elements, the presence of liquid film between cells, a wide critical temperature range, and the presence of thermal or residual stress. These prerequisites are present in L-PBF processes. The phases found in L-PBF-manufactured γ′-strengthened superalloys closely resemble those of the equivalent cast materials, where γ, γ′, and γ/γ′ eutectic and carbides are typically present in the microstructure. Additionally, the sizes of the γ′ particles are small in as-built L-PBF materials because of the high cooling rate. Furthermore, the creep performance of L-PBF-manufactured materials is inferior to that of cast material because of the presence of defects and the small grain size in the L-PBF materials; however, some vertically built L-PBF materials have demonstrated creep properties that are close to those of cast materials.© 2020 by the authors. Licensee MDPI, Basel, Switzerland.