Development of softwood kraft lignin based carbon fibers
Luleå University of Technology, Department of Engineering Sciences and Mathematics, Material Science.
2012 (English)Licentiate thesis, comprehensive summary (Other academic)
Abstract [en]

The polymer composites designed for high-performance applications are mostly based on carbon fiber reinforcement. The two most common precursors used currently for carbon fiber production are poly(acrylonitrile) and pitch (petroleum- or coal- based). As of today, the most promising alternative to these fossil originated raw materials is lignin. Previous research has mainly focused on carbon fiber production from pre-treated hardwood lignin with the addition of different softening agents. Softwood lignin has been considered difficult to melt, and thus, impossible to process by conventional melt spinning processes.The aim of the presented work is to find the way for melt spinning of softwood kraft lignin, by using lignin-derived additives. A method for isolation of kraft lignin was recently developed, making large amounts of high purity lignin available. The thermal properties of this type of lignin make it an interesting candidate for carbon fiber production. During this study, both unfractionated hardwood and softwood kraft lignin were used with addition of their fractionated counterparts, acting as softening agents. The spinning process of the lignin blends was optimized by adapting the processing temperature to the thermal properties of blends of different compositions. Different batches of lignin fibers were produced and characterized with scanning electron microscopy to evaluate the fiber diameter, the surface smoothness, the presence of pores and the shape of fiber cross-section.The fiber batch containing softwood kraft lignin and 10% fractionated hardwood kraft lignin was relatively easy to melt spin, despite the small amount of added fractionated hardwood lignin. Therefore, this batch was further processed into carbon fibers by oxidative stabilisation followed by carbonization in nitrogen atmosphere. X-Ray/Energy Dispersive Spectroscopy confirmed that carbon fibers containing above 90% carbon had been obtained. Mechanical characterization of produced lignin based carbon fibers was carried out. Single fiber tensile tests were performed to evaluate the stiffness and the strength of carbon fibers. In order to determine the properties of the lignin-based CFs, and to estimate the impact of the manufacturing parameters (such as die sizes and winding speeds), fibers of different diameters (≈30, 60 and 90 microns) were made and tested.Carbon fibers are brittle materials and therefore the experimental results (fiber strength) were treated by use of Weibull statistical distribution. Three fiber lengths (10, 20 and 40 mm) for each diameter were tested and strength data was approximated by two-parameter Weibull equation in order to obtain parameters of the strength distribution. The experimental results and predictions based on Weibull statistics showed a good fit.Although strength of the produced fibers is still significantly lower than that of commercially available carbon fibers, this thesis reports the first mechanical characterization of softwood kraft lignin based CFs.The carbon fiber production process differs depending on the raw material used. Most of the studies on lignin have considered hardwood lignin as raw material. As a first step towards a process optimized for softwood kraft lignin based carbon fibers, the stabilization step in the carbon fiber process was developed further.

Place, publisher, year, edition, pages
Luleå: Luleå tekniska universitet, 2012. , 101 p.
Licentiate thesis / Luleå University of Technology, ISSN 1402-1757
Research subject
Polymeric Composite Materials
URN: urn:nbn:se:ltu:diva-18370Local ID: 84529945-e5bc-41d7-b8e9-330cc6f3f2ccISBN: 978-91-7439-531-0OAI: diva2:991378
Godkänd; 2012; 20121115 (ylvnor); LICENTIATSEMINARIUM Ämne: Polymera konstruktionsmaterial/Polymeric Composite Materials Examinator: Professor Roberts Joffe, Institutionen för teknikvetenskap och matematik, Luleå tekniska universitet Diskutant: Professor Mikael Skrifvars, Högskolan i Borås Tid: Tisdag den 18 december 2012 kl 10.15 Plats: E231, Luleå tekniska universitetAvailable from: 2016-09-29 Created: 2016-09-29Bibliographically approved

Open Access in DiVA

fulltext(9385 kB)8 downloads
File information
File name FULLTEXT01.pdfFile size 9385 kBChecksum SHA-512
Type fulltextMimetype application/pdf

Search in DiVA

By author/editor
Nordström, Ylva
By organisation
Material Science

Search outside of DiVA

GoogleGoogle Scholar
Total: 8 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 36 hits
ReferencesLink to record
Permanent link

Direct link