Zeolite macrostructures
Luleå tekniska universitet.
1999 (English)Licentiate thesis, comprehensive summary (Other academic)
Abstract [en]

The preparation of zeolite macrostructures in the form of bilayered hollow tubes and microspheres is presented. The bilayered hollow ZSM-5/silicalite-1 tubes were prepared using carbon fibers as a substrate. The surface of the fibers was modified and colloidal silicalite-1 seed crystals adsorbed. The fibers were then treated with a synthesis mixture yielding ZSM-5. After separation of the fiber/zeolite composites a second treatment resulting in the crystallization of silicalite-1 was performed. Finally, the carbon fibers were removed by calcination leaving hollow tubes. Silicalite-1 micropsheres were prepared using macroporous anion exchange resins as shape directing macro-templates. Resin beads were hydrothermally treated with a synthesis solution yielding silicalite-1 resulting in the crystallization of silicalite-1 in the pores of the resin. The resin was then removed by calcination leaving self-bonded silicalite-1 micropsheres identical in shape and size to the original resin beads. The zeolite macrostructures were extensively characterized using SEM, XRD, EDS-analysis, Raman spectroscopy, nitrogen adsorption and microhardness measurements.

Place, publisher, year, edition, pages
Luleå tekniska universitet, 1999. , 18 p.
Series
Licentiate thesis / Luleå University of Technology, ISSN 1402-1757 ; 1999:27
Research subject
Chemical Technology
Identifiers
URN: urn:nbn:se:ltu:diva-17951Local ID: 6030cd80-d861-11db-a1bf-000ea68e967bOAI: oai:DiVA.org:ltu-17951DiVA: diva2:990957
Note
Godkänd; 1999; 20070322 (ysko)Available from: 2016-09-29 Created: 2016-09-29Bibliographically approved

Open Access in DiVA

fulltext(1805 kB)0 downloads
File information
File name FULLTEXT01.pdfFile size 1805 kBChecksum SHA-512
2548aaa7b6cf51ee094b86b54153f81cd132b0c823af96136e21a13bd7e8820137f6aaeb9c976ec039efcd47edc6fd028bbe03031df3de5001e5fd8c3c9bfc41
Type fulltextMimetype application/pdf

Search outside of DiVA

GoogleGoogle Scholar
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 4 hits
ReferencesLink to record
Permanent link

Direct link