Ultra-Low Density Fibreboard with Improved Fire Retardance and Thermal Stability using a Novel Fire- Resistant Adhesive
2016 (English)In: BioResources, ISSN 1930-2126, E-ISSN 1930-2126, Vol. 11, no 2, 5215-5229 p.Article in journal (Refereed) Published
A novel fire-resistant adhesive made from polyvinyl alcohol, urea, phosphoric acid, and starch was demonstrated for use as a binder and fire retardant to produce ultra-low density fibreboard (ULDF) with clear environmental benefits. The results from Fourier transform infrared spectroscopy showed the presence of chemical bonding between fire- resistant adhesives and ULDFs. The limiting oxygen index (LOI), combustion behaviour, and thermal stability were characterized using a LOI text, cone calorimeter, and thermal analyzer, respectively. The results demonstrated that the LOI value of the fire-retardant ULDF can reach up to 34.2 with 300 mL of fire-resistant adhesive. It was established that the additive noticeably reduced the peak of heat release rate, total heat release, and total smoke release of ULDF. Their morphologies after combustion were elucidated using a scanning electron microscope, and a char layer in the condensed phase was observed. Thermal analysis showed that the thermal stability of ULDF improved dramatically and the residual weight increased 4-fold, to 48.32%. Therefore, such ULDFs will be tremendously attractive as renewable, sustainable, and bio-based insulating materials.
Place, publisher, year, edition, pages
2016. Vol. 11, no 2, 5215-5229 p.
Research subject Wood Technology
IdentifiersURN: urn:nbn:se:ltu:diva-11206Local ID: a1ee7a4b-c0e8-4d0c-934f-12da3ce66b3dOAI: oai:DiVA.org:ltu-11206DiVA: diva2:984155
Validerad; 2016; Nivå 2; 20160331 (aliwan)2016-09-292016-09-29Bibliographically approved