Analysis and characterization of environmental friendly trivalent chromium passivation of aluminum alloys
Linköping University, Department of Physics, Chemistry and Biology.
Linköping University, Department of Physics, Chemistry and Biology.
2016 (English)Independent thesis Advanced level (degree of Master (Two Years)), 20 credits / 30 HE creditsStudent thesis
Abstract [en]

As of 21st September 2017, industrial use of hexavalent chromium (Cr(VI)) will, due to its environmental toxicity and carcinogenicity, be restricted by REACH regulations. Saab Aeronautics is therefore shifting anticorrosion surface treatment of aluminum alloys from hexavalent chromium conversion to trivalent chromium (Cr(III)) passivation. The purpose of this thesis is to investigate the characteristics of conversion coatings formed with the passivation chemical SurTec 650V, in order to facilitate transfer to the more environmental friendly alternative. Process parameters, such as pH and immersion time in SurTec 650V passivation baths, have been investigated for passivation of three different aluminum alloys; 2024, 6061 and 7075. The characteristics of the Cr(III) conversion coatings achieved at laboratory scale in the thesis work have been compared with SurTec 650V process in production scale and with Cr(VI) containing Alodine 1200 and Alodine 1500 processes.

The impact of varying process parameters have been investigated with goniometry, x-ray photoelectron spectroscopy (XPS), auger electron spectroscopy (AES), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) to analyse characteristics of the conversion coatings. Differences in chemical composition on the surface and in depth profile was detected with XPS and AES, respectively and topology of coatings was found to differ for different aluminium alloys and parameter combinations. With TEM, the thickness of the conversion coating was found to be approximately 30-50 nm, which is thinner than the coatings formed with Cr(VI) passivation. Characteristics of coatings formed with Cr(III) passivation is concluded to be very dependent on parameter variation, especially for alloy 2024. Differences also occur between passivation at laboratory and production scale. Further evaluation of the production scale SurTec 650V process and corrosion testing should be performed, and an elaboration of a process control is required before the shift to an environmental friendly passivation process can be completely successful at Saab.

Place, publisher, year, edition, pages
2016. , 81 p.
Keyword [en]
aluminium alloys, trivalent chromium passivation, SurTec 650V, goniometry, XPS, AES, SEM, TEM, corrosion
National Category
Other Materials Engineering
Identifiers
URN: urn:nbn:se:liu:diva-129351ISRN: LITH-IFM-A-EX--16/3244--SEOAI: oai:DiVA.org:liu-129351DiVA: diva2:938346
External cooperation
Saab Aeronautics
Subject / course
Biotechnology
Presentation
2016-06-08, Planck, Fysikhuset, Campus Valla, Linköpings universitetet, Linköping, 10:00 (Swedish)
Supervisors
Examiners
Available from: 2016-08-17 Created: 2016-06-16 Last updated: 2016-08-17Bibliographically approved

Open Access in DiVA

fulltext(5872 kB)27 downloads
File information
File name FULLTEXT01.pdfFile size 5872 kBChecksum SHA-512
66cc0b8ebc8d0900d05d184b22f2c2ce7556bd25cc8d3137e84cc938decdb2503d88b1668f9b6c06c463145f1d0fc905c4712f2fe4526d2154e058b1a4b5f81a
Type fulltextMimetype application/pdf

Search in DiVA

By author/editor
Västerlund, EmmaFlink, Ronja
By organisation
Department of Physics, Chemistry and Biology
Other Materials Engineering

Search outside of DiVA

GoogleGoogle Scholar
Total: 27 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 39 hits
ReferencesLink to record
Permanent link

Direct link