Parameters affecting dephosphorization of stainless steel
KTH, School of Industrial Engineering and Management (ITM), Materials Science and Engineering.
KTH, School of Industrial Engineering and Management (ITM), Materials Science and Engineering.
2015 (English)Independent thesis Basic level (degree of Bachelor), 10 credits / 15 HE creditsStudent thesis
Abstract [en]

A literary study has been made to find parameters affecting dephosphorization of stainless steel. Ways to lower phosphorus content without major loss of chromium in order to decrease the production costs of Sandvik AB’s stainless steel. The study was conducted with respect to oxidizing dephosphorization and parameters affecting dephosphorization are carbon and chromium content, temperature and slag properties. It was revealed that higher carbon content and basicity is beneficial to the dephosphorization process. However, the choice of temperature, chromium content and flux were dependant on which way dephosphorization was approached. A method of refining chromium in slag using an electric arc furnace (EAF) was also discovered. This made it possible to extract 97% of all chromium in slag. The conclusions are that in order for Sandvik to successfully remove phosphorus, scrap metal with higher carbon content should be used, together with a basic CaO slag with constituents of e g Li2O3 and CaF2. A deslagging step can be added to the argon oxygen decarburizer (AOD) process in order to remove the phosphorus bound to the slag, before decarburization.

Place, publisher, year, edition, pages
Keyword [en]
dephosphorization, stainless steel
National Category
Metallurgy and Metallic Materials
URN: urn:nbn:se:kth:diva-171426OAI: diva2:843950
External cooperation
Sandvik AB
Available from: 2016-09-30 Created: 2015-08-02 Last updated: 2016-09-30Bibliographically approved

Open Access in DiVA

fulltext(587 kB)5 downloads
File information
File name FULLTEXT01.pdfFile size 587 kBChecksum SHA-512
Type fulltextMimetype application/pdf

Search in DiVA

By author/editor
Wendel, Erik
By organisation
Materials Science and Engineering
Metallurgy and Metallic Materials

Search outside of DiVA

GoogleGoogle Scholar
Total: 5 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 9 hits
ReferencesLink to record
Permanent link

Direct link