Hydrogen induced stress cracking of alloy 718: Effects of chemical composition and microstructure
Norwegian University of Science and Technology, Faculty of Natural Sciences and Technology, Department of Materials Science and Engineering.
2014 (English)MasteroppgaveStudent thesis
Abstract [en]

This master thesis have examined the effect of variations in composition and microstructure on the HISC susceptibility of Inconel-718. 6 different Inconel-718 variants with different compositions and heat treatments were examined. Tensile samples were pre-charged with hydrogen at 120*C in an Orthophosphoric-acid/Glycerol electrolyte for 5 days, and subsequently subjected to stepwise constant-load tensile tests. The tensile tests were performed in synthetic saltwater with a negative polarization of -1050mA Ag/AgCl, corresponding to a galvanic coupling with aluminium or zinc in seawater. Hydrogen free samples were tested in air for comparison. An optical microscope was used to examine the sample surfaces during testing. Fracture surfaces were examined in SEM, and the samples were also examined for secondary cracks. All the Inconel-718 samples pre-charged with hydrogen showed a significant reduction in ductility and contained Inter Granular (IG) areas on the fracture surfaces. A decrease in fracture strength of approx. 5-10% of Yield Strength (YS) was seen in all the variants examined, but no significant trend between the Inconel-718 variants was detected here. Smaller grain sizes were correlated with an increasing ductility loss measured by loss of Reduction of Area (RA) and loss of Elongation prior to fracture. This was attributed to increased Grain Boundary (GB) diffusion of hydrogen during pre-charging, resulting from more GB areas. A Hydrogen melt extraction analysis done by SINTEF confirmed the elevated hydrogen levels expected in these fine-grained Inconel-718 variants.

Place, publisher, year, edition, pages
Institutt for produktutvikling og materialer , 2014. , 141 p.
URN: urn:nbn:no:ntnu:diva-26332Local ID: ntnudaim:11925OAI: diva2:746557
Available from: 2014-09-12 Created: 2014-09-12 Last updated: 2014-09-12Bibliographically approved

Open Access in DiVA

fulltext(85090 kB)318 downloads
File information
File name FULLTEXT01.pdfFile size 85090 kBChecksum SHA-512
Type fulltextMimetype application/pdf
cover(398 kB)26 downloads
File information
File name COVER01.pdfFile size 398 kBChecksum SHA-512
Type coverMimetype application/pdf
attachment(26085 kB)7 downloads
File information
File name ATTACHMENT01.zipFile size 26085 kBChecksum SHA-512
Type attachmentMimetype application/zip

By organisation
Department of Materials Science and Engineering

Search outside of DiVA

GoogleGoogle Scholar
Total: 318 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 77 hits
ReferencesLink to record
Permanent link

Direct link