Chemical Modification of NFC: Development of Renewable Barriers for Packaging Applications
KTH, School of Chemical Science and Engineering (CHE).
2012 (English)Independent thesis Advanced level (professional degree), 20 credits / 30 HE creditsStudent thesis
Abstract [en]

Globalization and centralization have resulted in prolonged transportation time between producer and consumer, and thus put more demand on the perseveration of a product for longer duration and protect it from oxidation. The presence of oxygen in packages severely foreshortens the storage life as it yield losses of nutrients and allow microbial growth, which can cause changes in smell, taste as well as discoloration. Earlier food and beverage containers were made in inorganic materials e.g. metal and glass, however lately more and more focus have been on synthetic organic materials as these show several advantages, e.g. weight. However, still today most of the commercial packaging materials, organic or inorganic, are not considered to be environmental friendly. Thus, efforts have to be made today in order to invent alternative materials that can make the society of tomorrow more sustainable. Cellulose is the most abundant biopolymer in the world, hence making it desirable to use in “green” packaging applications. Furthermore, cellulose has proven being able to form films with great gas barrier potential under specific conditions. However, cellulose based materials are sensitive to moisture with severely increased oxygen transmission with increased relative humidity as a result; hence it is desired to make cellulose less hygroscopic by chemical modification. First, nanofibrillated cellulose (NFC) with 720 mmol carboxylic groups/g fiber was produced by oxidation of dissolving pulp before homogenization. Thereafter a polymer was synthesized utilizing Initiator A as an initiator at T1 and T2. The polymer synthesized at T1 yielded a polymer with a viscosity average molecular weight of 5770 g/mol.  The polymer was then grafted on the oxidized NFC through a coupling reaction performed in Buffer C using Coupling agent A. The grafting procedure was performed in Buffer C at ambient conditions giving rise to a material composed of 33 wt% synthetic polymer and 67 wt% NFC. The coupling was conducted several times in order to investigate how the final product can be affected by varying reactant feed and dispersion method. Finally, films of NFC and NFC-g-Polymer were manufactured by vacuum filtration from a 0.05 wt% Solvent A dispersion and were evaluated with field emission scanning electron microscopy.

Place, publisher, year, edition, pages
2012. , 43 p.
Keyword [en]
Packaging; nanofibrillated cellulose (NFC); polymer modification; grafting; biocomposite
National Category
Engineering and Technology
URN: urn:nbn:se:kth:diva-146309OAI: diva2:723768
Available from: 2014-06-12 Created: 2014-06-11 Last updated: 2014-06-12Bibliographically approved

Open Access in DiVA

fulltext(1708 kB)140 downloads
File information
File name FULLTEXT01.pdfFile size 1708 kBChecksum SHA-512
Type fulltextMimetype application/pdf

By organisation
School of Chemical Science and Engineering (CHE)
Engineering and Technology

Search outside of DiVA

GoogleGoogle Scholar
Total: 140 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 639 hits
ReferencesLink to record
Permanent link

Direct link