Contacts to P-doped GaAs Nanowires by Fabrication of Electrodes using Metals and Graphene
Norwegian University of Science and Technology, Faculty of Information Technology, Mathematics and Electrical Engineering, Department of Electronics and Telecommunications.
2012 (English)MasteroppgaveStudent thesis
Abstract [en]

P-type GaAs semiconducting nanowires (NWs) with NW/electrode contacts have been examined by fabricating single NW devices to investigate their electrical properties. Both NWs grown with Au-assisted and Ga-assisted vapor-liquid-solid (VLS) method have been examined, with great emphasis on Ga-assisted NWs because these show superior contact properties. The NWs were grown using molecular beam epitaxy (MBE) and electrical contacts were fabricated using electron beam litography, electron beam evaporation for metallization and annealing to enhance ohmic behaviour of the contacts. Two different types of contacts were tested. One was metal contacts where various combinations of metal layers were tested, including such metallizations as Pt/Ti/Pt/Au and Pd/Zn/Pd/Au. The second electrode type was graphene which is expected to show very interesting electric and optoelectronic properties. It is shown in this thesis that ohmic contact with linear I-V characteristics has been achieved by two different methods. The first being annealing of the NW contact after contact fabrication. The second is by increasing doping concentration during NW growth. It is also shown that Pt/Ti/Pt/Au metallization is the layer configuration that exhibits the best ohmic contact and the most consistency in electrical measurements. 4-probe measurements were also carried out to measure the intrinsic resistivity of the NW, which makes it possible to estimate its doping concentration and carrier mobility. NW/graphene contact was also tried.Mechanical exfoliation of kish graphite was performed to make high-quality graphene, which was selctively placed to make NW contact. However it is found that heating of the EBL-resist during e-beam evaporation caused the graphene to wrinkle and dissolve. CVD-grown graphene on Cu-foil was also tested. Inspection after the graphene transfer proved that the graphene that was used was incontinous and flaky making it difficult to obtain proper contacts to NWs. In addition the NWs connected to graphene probably suffered from over-etching due to multiple etching steps. Since a lot of efforts was put into obtaining a suitable measure of making NW/graphene contacts only preliminary measurements were conducted, so these results has yet to be verified.

Place, publisher, year, edition, pages
Institutt for elektronikk og telekommunikasjon , 2012. , 71 p.
Keyword [no]
ntnudaim:7532, MTEL elektronikk, Nanoelektronikk og mikrosystemer
URN: urn:nbn:no:ntnu:diva-18846Local ID: ntnudaim:7532OAI: diva2:566316
Available from: 2012-11-08 Created: 2012-11-08

Open Access in DiVA

fulltext(21324 kB)664 downloads
File information
File name FULLTEXT01.pdfFile size 21324 kBChecksum SHA-512
Type fulltextMimetype application/pdf
cover(1069 kB)76 downloads
File information
File name COVER01.pdfFile size 1069 kBChecksum SHA-512
Type coverMimetype application/pdf

By organisation
Department of Electronics and Telecommunications

Search outside of DiVA

GoogleGoogle Scholar
Total: 664 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 82 hits
ReferencesLink to record
Permanent link

Direct link