HF Formation Upon Addition of Different Industrial Aluminas to Cryolitic Baths
Norwegian University of Science and Technology, Faculty of Natural Sciences and Technology, Department of Chemistry.
2011 (English)MasteroppgaveStudent thesis
Abstract [en]

The aluminium smelter at Hydro Sunndal has experienced problems with an unexpected increased loss of AlF3 from the electrolyte when using a certain quality of alumina. One hypothesis considered was that the fluoride loss was a direct result of unusually high HF formation when the quality was added to the cryolitic melt. This work has set out to study the HF formation potential of three different industrial alumina qualities. Alumina A was an alumina quality that worked well in the smelter. Alumina B was the alumina quality where the aforementioned drop in AlF3 was observed and alumina C, made by the same producer, controversially did not to exhibit the same loss at smelter. The present work has been divided into two parts: a characterisation section, where the aluminas have been characterised by techniques such as LOI, TGA, DSC and XRD, and an experimental section, where the industrial aluminas were added to a cryolitic melt. The HF formation and the corresponding H2O concentration were measured in-situ using a tunable diode laser during the alumina additions to the cryolitic melt. Through this work it has been found that both primary and secondary alumina A form less HF than alumina B and C. The LOI, TGA and XRD characterisation has shown that alumina B and C contain a substantial amount of gibbsite, whilst the gibbsite level in alumina A is negligible. A clear correlation between the quantity of moisture found through LOI characterisation and HF formation has been found. It has also been shown that all types of moisture found through LOI testing contribute to HF formation; both physisorbed and chemisorbed types, as well as structural hydroxyl. From the present work it cannot be explained why alumina B caused a drop in AlF3 in the electrolyte, whilst alumina C did not. One explanation postulated is that alumina C has better scrubber efficiency than alumina B. Examining this hypothesis has been outside the scope of this master work. If variations in scrubber efficiency for the two aluminas fail to explain the drop in AlF3, the solution may be found in parameters outwit the alumina quality e.g. weather conditions at the time of production or storage conditions at the calciner.

Place, publisher, year, edition, pages
Institutt for materialteknologi , 2011. , 118 p.
Keyword [no]
ntnudaim:6637, MTKJ Industriell kjemi og bioteknologi, Materialer for energiteknologi
URN: urn:nbn:no:ntnu:diva-18335Local ID: ntnudaim:6637OAI: diva2:566046
Available from: 2012-11-08 Created: 2012-11-08 Last updated: 2013-06-23Bibliographically approved

Open Access in DiVA

fulltext(4417 kB)544 downloads
File information
File name FULLTEXT01.pdfFile size 4417 kBChecksum SHA-512
Type fulltextMimetype application/pdf
cover(47 kB)22 downloads
File information
File name COVER01.pdfFile size 47 kBChecksum SHA-512
Type coverMimetype application/pdf

By organisation
Department of Chemistry

Search outside of DiVA

GoogleGoogle Scholar
Total: 544 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 76 hits
ReferencesLink to record
Permanent link

Direct link