Wet-chemical deposition of silicon quantum dots for enhanced solar cell efficiency
Norwegian University of Science and Technology, Faculty of Natural Sciences and Technology, Department of Materials Science and Engineering.
2011 (English)MasteroppgaveStudent thesis
Abstract [en]

Silicon quantum dots were synthesised wet-chemically by three different methods based on reduction of silicon tetrachloride with the reduction agents potassium naphthalide, sodium cyclopentadiene and the alkalide of potassium. The purpose of these quantum dots was to deposit them on a substrate in order to use them as down converters on top of photovoltaic solar cells for enhanced solar cell efficiency. One possible method for the formation of down converting layers is to incorporate quantum dots into silica thin films by deposition of quantum dots in an ethanol based silica sol, followed by spin coating. It is believed that when the quantum dots are water dispersible, this will make it easier to bind them to the silica network, and a good dispersion in the film is facilitated. The different hydrophilic functionalisations investigated were pentenoxy capping, oxidised pentenoxy capping, oxidised acrylic acid capping and ethanolamine capping. Challenges were encountered during the synthesis of water dispersible quantum dots, the most important were related to agglomeration and purification of the quantum dots. This was believed to be due to the tendency of hydrophilic surface groups to attract each other, interaction with the polar solvent and similar solubility characteristics of the quantum dots and the byproduct salts. Si quantum dots with hydrophobic octoxy capping were also synthesised. Dispersions of these quantum dots were deposited onto solid substrates followed by solvent evaporation. This was done to see whether it was possible to deposit the synthesised quantum dots by this simple approach, to investigate the fundamentals upon evaporation, the degree of agglomeration and the byproducts present in the quantum dot dispersions. It was found that agglomeration was very pronounced after the solvent had evaporated and that quite large amounts of byproducts were present in the final quantum dot dispersions. The most important reasons to this were believed to be too weak steric repulsive forces between the particles, too fast evaporation of the solvent and an insufficient purification procedure. For the use of Si quantum dots synthesised wet-chemically as down converters in solar cells, improvements of the particles are needed.

Place, publisher, year, edition, pages
Institutt for materialteknologi , 2011. , 87 p.
Keyword [no]
ntnudaim:6528, MTKJ Industriell kjemi og bioteknologi, Materialer for energiteknologi
URN: urn:nbn:no:ntnu:diva-16318Local ID: ntnudaim:6528OAI: diva2:517079
Available from: 2012-04-20 Created: 2012-04-20

Open Access in DiVA

fulltext(22259 kB)1149 downloads
File information
File name FULLTEXT01.pdfFile size 22259 kBChecksum SHA-512
Type fulltextMimetype application/pdf
cover(47 kB)40 downloads
File information
File name COVER01.pdfFile size 47 kBChecksum SHA-512
Type coverMimetype application/pdf

By organisation
Department of Materials Science and Engineering

Search outside of DiVA

GoogleGoogle Scholar
Total: 1149 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 148 hits
ReferencesLink to record
Permanent link

Direct link