Phase Stability and Elasticity of TiAlN
Linköping University, Department of Physics, Chemistry and Biology, Theoretical Physics. Linköping University, The Institute of Technology.
Linköping University, Department of Physics, Chemistry and Biology, Nanostructured Materials. Linköping University, The Institute of Technology.
Linköping University, Department of Physics, Chemistry and Biology, Theoretical Physics. Linköping University, The Institute of Technology.
Linköping University, Department of Physics, Chemistry and Biology, Theoretical Physics. Linköping University, The Institute of Technology.
Show others and affiliations
2011 (English)In: Materials, ISSN 1996-1944, Vol. 4, no 9, 1599-1618 p.Article in journal (Refereed) Published
Abstract [en]

We review results of recent combined theoretical and experimental studies of Ti1−xAlxN, an archetypical alloy system material for hard-coating applications. Theoretical simulations of lattice parameters, mixing enthalpies, and elastic properties are presented. Calculated phase diagrams at ambient pressure, as well as at pressure of 10 GPa, show a wide miscibility gap and broad region of compositions and temperatures where the spinodal decomposition takes place. The strong dependence of the elastic properties and sound wave anisotropy on the Al-content offers detailed understanding of the spinodal decomposition and age hardening in Ti1−xAlxN alloy films and multilayers. TiAlN/TiN multilayers can further improve the hardness and thermal stability compared to TiAlN since they offer means to influence the kinetics of the favorable spinodal decomposition and suppress the detrimental transformation to w-AlN. Here, we show that a 100 degree improvement in terms of w-AlN suppression can be achieved, which is of importance when the coating is used as a protective coating on metal cutting inserts.

Place, publisher, year, edition, pages
MDPI , 2011. Vol. 4, no 9, 1599-1618 p.
Keyword [en]
hard coatings; spinodal decomposition; ab initio calculations; thermodynamics; multilayer; TiN
National Category
Manufacturing, Surface and Joining Technology
URN: urn:nbn:se:liu:diva-72927DOI: 10.3390/ma4091599ISI: 000298245900006OAI: diva2:463705
Strategic Initiative - Materials Science

Funding agencies|Swedish Foundation for Strategic Research (SSF) via research center MultiFilms||Swedish Foundation for Strategic Research (SSF) via research center MS2E||Swedish Research Council (VR)||

Available from: 2011-12-11 Created: 2011-12-11 Last updated: 2016-08-31
In thesis
1. Theoretical understanding of stability of alloys for hard-coating applications and design
Open this publication in new window or tab >>Theoretical understanding of stability of alloys for hard-coating applications and design
2015 (English)Doctoral thesis, comprehensive summary (Other academic)
Abstract [en]

The performance of modern hard coating materials puts high demands on properties such as hardness, thermal stability and oxidation resistance. These properties not only depend on the chemical composition, but also on the structure of the material on a nanoscale. This kind of nanostructuring will change during use and can be both beneficial and detrimental as materials grown under non-equilibrium conditions transforms under heat treatment or pressure into other structures with significantly different properties. This thesis aims to reveal the physics behind the processes of phase stability and transformations and how this can be utilized to improve on the properties of this class of alloys. This has been achieved through the application of various methods of first-principles calculations and analysis of the results on the basis of thermodynamics and electronic structure theory.

Within multicomponent transition metal aluminum nitride alloys (TMAlN) a number of studies have been carried out and presented here on ways of improving high temperature stability and hardness. Most (TMAl)N and TMN prefer a cubic B1 structure while AlN is stable in a hexagonal B4 phase, but for the purposes of hard coatings the metastable cubic B1 AlN phase, isostructural with the TMN phase is desired. It will be shown how the introduction of additional alloying components, such as Cr, into (TiAl)N changes the thermodynamic stability of phases so that new intermediary and metastable phases are formed during decomposition. In the case of such a (CrAl)N phase it is shown to have greater thermodynamic stability in the cubic phase than the pure AlN, resulting in improved high temperature hardness. Also, the importance of treating not just the binodal decomposition through the formation energy relative to end products but also the impact of spinodal decomposition from its second derivative due to the topology of formation energy surfaces is emphasized in the thesis. The impact of pressure on the AlN phase has also been studied through the calculation of a P-T diagram of AlN as part of a (TiAl)N alloy.

During the study of chemical alloying of TM components into AlN the alloying of low concentrations of these TM were treated in great detail. What is generally referred to as the AlN phase in decomposition is not entirely pure and can be expected to contain traces of any alloying components, such as Ti and Cr or whatever other metals may be present. Low concentration alloying of Cr, on the order of 5-10% is also shown to be stable with regard to isostructural decomposition. Detailed analysis of the effect of Ti and Cr impurities in AlN has been carried out along with a systematic search of AlN alloyed with small amounts of other TM components. The impact of these impurities on the electronic structure and thermodynamic properties is analyzed and the general trends will be explained through the occupation of impurity states by d-like electrons.

Theoretical treatment of such impurities is not straightforward however. AlN is an s-p semiconductor with a wide band gap while TM impurities generate states of a d-like nature situated inside the band gap. Such localized impurity states are expected to give rise to magnetic effects due to spin dependent exchange, in addition strong correlation effects might have to be taken into account. For that reason the use of hybrid functionals with orbital corrections according to the mHSE+Vw scheme, developed specifically for this class of materials, has been used and shown to influence the results during calculation of impurities of Ti and Cr.

In nanocomposite multilayered structures, composed of very thin layers of one material sandwiched between slabs of another, such as layers of SiN between TiN or ZrN, the material properties are greatly affected by the interfaces. In addition to the thermodynamic effects and lattice strains of the interfaces one also has to consider the atomic vibrational motion in the interface structure. Hence, dynamical stability of these thin multilayers is of great importance. As part of this thesis, results on the thermodynamic and dynamical stability of both TiN-SiN layers and ZrN-SiN will be presented. It will be shown that due to considerable dynamical instability in the interface structure of monolayered B1 SiN sandwiched between isostructural layers of B1 ZrN along (111) interfaces this structure cannot be expected to grow, instead preferring the stable (001) direction of growth.

Place, publisher, year, edition, pages
Linköping: Linköping University Electronic Press, 2015. 73 p.
Linköping Studies in Science and Technology. Dissertations, ISSN 0345-7524 ; 1647
National Category
Physical Sciences Materials Engineering
urn:nbn:se:liu:diva-115405 (URN)10.3384/diss.diva-115405 (DOI)978-91-7519-112-6 (print) (ISBN)
Public defence
2015-04-10, Planck, Fysikhuset, Campus Valla, Linköping, 13:15 (English)
Available from: 2015-03-16 Created: 2015-03-16 Last updated: 2015-03-16Bibliographically approved

Open Access in DiVA

fulltext(860 kB)103 downloads
File information
File name FULLTEXT01.pdfFile size 860 kBChecksum SHA-512
Type fulltextMimetype application/pdf

Other links

Publisher's full text

Search in DiVA

By author/editor
Abrikosov, IgorKnutsson, AxelAlling, BjörnTasnádi, FerencLind, HansHultman, LarsOdén, Magnus
By organisation
Theoretical PhysicsThe Institute of TechnologyNanostructured MaterialsThin Film Physics
In the same journal
Manufacturing, Surface and Joining Technology

Search outside of DiVA

GoogleGoogle Scholar
Total: 103 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Altmetric score

Total: 427 hits
ReferencesLink to record
Permanent link

Direct link