Electrocodeposition of nano-SiC particles by pulse-reverse under an adapted waveform
Jönköping University, School of Engineering, JTH, Materials and Manufacturing.ORCID iD: 0000-0001-7228-1188
Jönköping University, School of Engineering, JTH, Materials and Manufacturing. RISE Research Institutes of Sweden, Borås, Sweden.ORCID iD: 0000-0002-7095-1907
Jönköping University, School of Engineering, JTH, Materials and Manufacturing.ORCID iD: 0000-0003-2924-137X
2019 (English)In: Journal of the Electrochemical Society, ISSN 0013-4651, E-ISSN 1945-7111, Vol. 166, no 15, p. D804-D809Article in journal (Refereed) Published
Abstract [en]

This work has explored the potential of using pulse reverse (PR) plating for increasing the deposited fraction of SiC nanoparticles. Two PR waveforms were selected, a short pulse (500 Hz) waveform and a newly modified and adapted pulsed sequence that equals the plating thickness to the particles’ diameter (50 nm) for the on-time and half-diameter during the anodic time. The pulse waveforms were designed with 4 and 10 A⋅dm−2 as the average current density and cathodic peak current density, respectively. Direct current (DC) deposits at the same values were also produced as reference. In all cases, the codeposition of nano-SiC particles influenced the microstructure. The electroplating under DC 10 A⋅dm−2 showed the strongest grain refinement and increased the content of the particles (up to 2% vol.) PR using high-frequency achieved a similar codeposition. The maximum particle incorporation was achieved by the proposed adapted pulse waveform, doubling the SiC content produced by other set-ups (up to 4% vol.); increasing the microhardness of the deposits to 400 HV, despite no grain refinement compared to the pure metal. From these results, it was observed a relationship between the influence of the plating method on the microstructure, the particle content, and the material's hardness.

Place, publisher, year, edition, pages
Electrochemical Society, 2019. Vol. 166, no 15, p. D804-D809
Keywords [en]
Electrodeposition, Composite coating, Electroplating, Pulse reverse current
National Category
Materials Engineering
Identifiers
URN: urn:nbn:se:hj:diva-46770DOI: 10.1149/2.0441915jesISI: 000494282300003Local ID: PP JTH 2019OAI: oai:DiVA.org:hj-46770DiVA, id: diva2:1367651
Note

Included in licentiate thesis in manuscript form with the title: "Codeposition of nano-SiC particles by pulse-reverse electroplating".

Available from: 2019-11-04 Created: 2019-11-04 Last updated: 2019-11-27Bibliographically approved
In thesis
1. Study of particle-current-electrocrystallization interactions in electroplating of Ni/SiC coatings
Open this publication in new window or tab >>Study of particle-current-electrocrystallization interactions in electroplating of Ni/SiC coatings
2019 (English)Licentiate thesis, comprehensive summary (Other academic)
Abstract [en]

Composite coatings have great potential due to the possibility to combine properties of two different materials in one coating. This way, new surface properties can be tailored and applied to any material's surface. Among different manufacturing routes, electrodeposition has the biggest potential in creating composite metal matrix coatings, especially nanocomposites. Nevertheless, there is a knowledge gap between the deposition of composite coatings in laboratory conditions, described in the literature, and those that are now in place on an industrial level. While micro-composites have been industrialised for about ten years, the production of Ni/SiC nanocomposite coatings by electroplating is still far from an industrial manufacturing floor. This is due to the lack of understanding of the mechanisms of nanoparticles codeposition leading to scattering results.

The production of nanocomposite coatings is much more sensitive to the process parameters compared to microcomposite. The correlation between parameters and their influence on the codeposition are still not fully identified and understood. The codeposition models proposed in the literature are only valid in specific conditions, but composite depositions behave differently, or even opposite if some of the variables are modified.

The main objective of this work is to identify the particle-current-electrocrystallization interactions in the production of Ni/SiC nanocomposites. A series of experiments are designed to isolate single variables and identify the controlling parameters of these interactions and their impact on the final properties.

In this thesis, the effect of current density, type of current and particles size are identified as primary variables controlling the metal crystallisation and coatings properties.

Among many parameters, a specific current waveform in pulse reverse mode proved to increase the codeposition rate effectively, doubling the content of nanoparticles compared to other techniques. Ultrasound assistance is also considered as stirring method when particles are suspended in the deposition bath to increase their stability and dispersion. The effect of Ultrasound on the particles codeposition and metal crystallisation is studied and compared to silent condition.

Moreover, a surface treatment for the particle has been proven successful in making any particle to behave similarly in the Ni deposition bath. Furthermore, the codeposition rate doubled or tripled compared to untreated ones thanks to this treatment. Both ultrasonic agitation and surface treatment reduce the formation of aggregates, improving the particle dispersion and metal microstructure thus increasing the final hardness.

The work proved the synergistic effect between particle and metal microstructure which affected the final properties of the coating. Therefore, when tailoring the composite coating to improve hardness, it is not only the amount of the particles that should be considered but also their influence on the electrocrystallisation process.

Abstract [sv]

Kompositbeläggning har stort potential tack vare möjligheten att kombinera två material i samma ytskikt. På detta sätt kan nya ytegenskaper skräddarsys och appliceras på ett materials yta. Elektrodeposition är den tillverkningsmetod som har störst potential att uppnå kompositbeläggningar, i synnerhet nanokompositer. Ett kunskapsgap existerar mellan elektrodeposition under laboratorieförhållanden, som beskrivet i vetenskaplig litteratur, och hur processen går till i industriell miljö. Medan industriell tillämpning av mikrokompositer pågått ungefär tio år, så har produktion av Ni/SiC nanokompositbeläggningar fortfarande inte nått fabriksgolvet. Detta är en konsekvens av bristande förståelse kring mekanismer för samdeposition av nanopartiklar som leder till varierande resultat.

Produktion av nanokompositbeläggningar är mycket mer känslig för processparametrar jämfört med mikrokompositer. Korrelationer mellan parametrar och dess inverkan på samdeposition är fortfarande inte fullt identifierade och förstådda. Modeller för samdeposition som föreslås i vetenskaplig litteratur är endast giltiga under särskilda förhållanden. Kompositdeposition kan uppvisa avvikande eller till och med motsatt beteende om variabler förändras.

Huvudmålet med detta arbete är att identifiera interaktioner mellan partikel, ström och elektrokristallisering under tillverkning av Ni/SiC nanokompositer. En serie av experiment är utvecklade för att isolera variabler och identifiera de parametrarna som kontrollerar dessa interaktioner och dess inverkan på ytans egenskaper.

I denna avhandling identifieras strömtäthet, typ av ström, och partiklars storlek som primära variabler som kontrollerar metallkristallisering och beläggningens egenskaper.

Bland många parametrar, visades en specifik vågform på strömmen i omvänd pulsläge öka samdepositionen effektivt, ledande till en fördubbling av andelen nanopartiklar jämfört med andra tekniker. Ultraljud tillämpades som metod för omrörning av depositionsbadet för förbättrad stabilitet och fördelning. Effekten av ultraljud på samdepositionen av metallkristallisering studeras och jämfört med tyst tillstånd.

Dessutom har en ytbehandling för partiklarna visats framgångsrik för att få godtyckliga partiklar att bete sig likt Ni i depositionsbadet. Detta ledde till att samdepositionens takt ökade med en faktor av två till tre jämfört med obehandlade partiklar. Både ultraljud och ytbehandling av partiklarna ledde till minskad aggregation vilket förbättrade fördelningen av partiklar och metallstruktur och därigenom ökad hårdhet.

Arbetet bevisar synergieffekten mellan partiklar och metallstruktur vilket påverkar beläggningens slutliga egenskaper. Vid utveckling av nya ytbeläggningar ska därför inte bara mängden partiklar beaktas utan även dess interaktion med elektrokristalliseringsprocessen.

Place, publisher, year, edition, pages
Jönköping: Jönköping University, School of Engineering, 2019. p. 45
Series
JTH Dissertation Series ; 039
Keywords
Composite coatings; Nanoparticles; Electrocrystallisation; Microstructure; Surface treatment; Pulse plating; Ultrasound agitation, Kompositbeläggningar; Nanopartiklar; Elektrokristallisering; Mikrostruktur; Ytbehandling; Pulsplätering; Ultraljudsomrörning
National Category
Mechanical Engineering
Identifiers
urn:nbn:se:hj:diva-43548 (URN)978-91-87289-41-5 (ISBN)
Supervisors
Available from: 2019-04-26 Created: 2019-04-26 Last updated: 2019-11-04Bibliographically approved

Open Access in DiVA

fulltext(1009 kB)25 downloads
File information
File name FULLTEXT01.pdfFile size 1009 kBChecksum SHA-512
0fd0a8baf419f84c15c80b29d28690a105b8efc145811634cbdd92f83f4e936a87c959dd7deec18afb95d761c43409ead702ab924d4159a7368f72838de7b6f3
Type fulltextMimetype application/pdf

Other links

Publisher's full text

Search in DiVA

By author/editor
Pinate, SantiagoLeisner, PeterZanella, Caterina
By organisation
JTH, Materials and Manufacturing
In the same journal
Journal of the Electrochemical Society
Materials Engineering

Search outside of DiVA

GoogleGoogle Scholar
Total: 25 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

doi
urn-nbn

Altmetric score

doi
urn-nbn
Total: 82 hits
CiteExportLink to record
Permanent link

Direct link
Cite
Citation style
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Other style
More styles
Language
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Other locale
More languages
Output format
  • html
  • text
  • asciidoc
  • rtf