Hierarchically porous binder-free silicalite-1 discs: a novel support for all-zeolite membranesVise andre og tillknytning
2011 (engelsk)Inngår i: Journal of Materials Chemistry, ISSN 0959-9428, E-ISSN 1364-5501, Vol. 21, nr 24, s. 8822-8828Artikkel i tidsskrift (Fagfellevurdert) Published
Abstract [en]
Thermal expansion mismatch between the zeolite film and the support is an important cause for the formation of defects and cracks during the fabrication and use of zeolite membranes. We have studied how silicalite-1 discs with a permeability comparable to commercially available alumina supports can be produced by pulsed current processing (PCP) as a novel substrate for all-zeolite membranes. Hierarchically porous and mechanically strong membrane supports where the surface area and crystallography of the silicalite-1 particles were maintained could be obtained by carefully controlling the thermal treatment during PCP consolidation. In situ X-ray diffraction and dilatometry showed that the coefficient of thermal expansion (CTE) of the silicalite-1 substrate was negative in the temperature range 200-800 degrees C while the commonly used alumina substrate displayed a positive CTE. The critical temperature variation, Delta T, and thicknesses for crack-free supported zeolite films with a negative CTE were estimated using a fracture energy model. Zeolite films with a thickness of 1 mu m can only sustain a relatively modest Delta T of 100 degrees when supported onto alumina substrates while the all-zeolite membranes can support temperature variations above 500 degrees
sted, utgiver, år, opplag, sider
2011. Vol. 21, nr 24, s. 8822-8828
HSV kategori
Forskningsprogram
Kemisk teknologi
Identifikatorer
URN: urn:nbn:se:ltu:diva-5059DOI: 10.1039/C1JM10584AISI: 000291352900049Scopus ID: 2-s2.0-79959201323Lokal ID: 313f4200-0ec3-45c4-83f5-3f300e11ebd8OAI: oai:DiVA.org:ltu-5059DiVA, id: diva2:977933
Merknad
Validerad; 2011; 20110617 (andbra)
2016-09-292016-09-292021-10-15bibliografisk kontrollert