The early stage of galling
Örebro universitet, Institutionen för naturvetenskap och teknik. Avdelningen för maskin- och materialteknik, Karlstads universitet, Karlstad, Sverige.ORCID-id: 0000-0002-8144-8821
2012 (engelsk)Licentiatavhandling, med artikler (Annet vitenskapelig)
Abstract [en]

In sheet metal forming (SMF) of materials such as stainless steels there is a major problem with transfer and accumulation of sheet material to the metal forming tool surface. The problem is known as galling; a kind of severe adhesive wear, which results in severe scratching of produced parts. In this thesis, galling observed in contacts between tool steels and stainless steel sheets under lubricated sliding conditions was studied, focusing on the early stage of galling. It was found that changes in friction cannot be used as galling indicator in the early stage of galling because transfer and accumulation of sheet material happens even though friction is low and stable. The progression of galling is influenced by tool steel damage occurring around the tool steel hard phases caused by sheet material flow, which results in formation of wear-induced galling initiation sites. A correlation between the critical contact pressure to galling and sheet material proof stress was found. Galling happened at lower pressures for sheet material with lower proof stress possibly due to easier sheet material flow, resulting in quicker tool damage. Material transfer and tool steel damage were delayed for tool steels comprising homogenously distributed, small and high hard phases. Additionally, the galling resistance was higher for tool steels with higher hardness due to decreased tool steel damage. In a comparison between observations of the worn tool surfaces after wear tests and calculations in FEM it was found that material transfer did not take place at regions with highest contact pressures but at regions with highest plastic strains. The results obtained in this thesis indicate that tool steel damage and sheet material flow occurring in the contact during sliding are important factors influencing galling.

sted, utgiver, år, opplag, sider
Karlstad: Karlstads universitet , 2012. , s. 41
Serie
Karlstad University Studies, ISSN 1403-8099 ; 51
Emneord [en]
Galling, Stainless steel, Tool steel, Friction, Sliding wear, SOFS, Tribology, Wear
HSV kategori
Forskningsprogram
Materialteknik
Identifikatorer
URN: urn:nbn:se:oru:diva-58823ISBN: 978-91-7063-462-8 (tryckt)OAI: oai:DiVA.org:oru-58823DiVA, id: diva2:1128233
Presentation
2012-12-07, Eva Erikssonsalen, 21A 342, Karlstads Universitet, 13:15 (engelsk)
Opponent
Veileder
Tilgjengelig fra: 2017-09-04 Laget: 2017-07-24 Sist oppdatert: 2018-05-15bibliografisk kontrollert

Open Access i DiVA

fulltekst(2395 kB)174 nedlastinger
Filinformasjon
Fil FULLTEXT01.pdfFilstørrelse 2395 kBChecksum SHA-512
426d53bcf83f543ef110662028db7a1dca27615ca64099a3b49f2ec79cdeaeedcda1ce81440b7fb57e40abb8ce2863b7af093ba4904b159211c9960159775beb
Type fulltextMimetype application/pdf

Andre lenker

PDF

Søk i DiVA

Av forfatter/redaktør
Karlsson, Patrik
Av organisasjonen

Søk utenfor DiVA

GoogleGoogle Scholar
Totalt: 174 nedlastinger
Antall nedlastinger er summen av alle nedlastinger av alle fulltekster. Det kan for eksempel være tidligere versjoner som er ikke lenger tilgjengelige

isbn
urn-nbn

Altmetric

isbn
urn-nbn
Totalt: 414 treff
RefereraExporteraLink to record
Permanent link

Direct link
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association-8th-edition
  • vancouver
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf